产品说明：

Main characteristics:
• High toughness
• Good heat resistance
• Glass-like transparency, optical quality
• High dimensional accuracy and stability

Grade characteristics:
• PC/UV absorber concentrate
• High viscosity; easy release
• Special grade for the coextrusion of Makrolon ET base resins

As of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – Covestro.

物性信息：

物理性能额定值 (公制)额定值 (英制)测试方法

密度	1.19 g/cc	0.0430 lb/in³	ISO 1183-1
熔体流动速率	11 g/10 min @Load 1.20 kg, Temperature 300 °C	11 g/10 min @Load 2.65 lb, Temperature 572 °F	ISO 1133

机械性能额定值 (公制)额定值 (英制)测试方法

简支梁无缺口冲击强度	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	ISO 179-1eU

电气性能额定值 (公制)额定值 (英制)测试方法

体积电阻率	1.00e+16 ohm-cm	1.00e+16 ohm-cm	IEC 60093
表面电阻	1.00e+16 ohm	1.00e+16 ohm	IEC 60093

热性能额定值 (公制)额定值 (英制)测试方法

载荷下热变形温度(0.46 MPa)	128 °C	262 °F	ISO 75-1,-2
载荷下热变形温度(1.8 MPa)	116 °C	241 °F	ISO 75-1,-2
维卡软化温度	134 °C @Load 5.10 kg	273 °F @Load 11.2 lb	50°C/h; ISO 306

加工性能额定值 (公制)额定值 (英制)测试方法

加工（熔体）温度	300 °C	572 °F	Injection molding; ISO 294
模具温度	80.0 °C	176 °F	Injection molding; ISO 294
射速	200 mm/sec	7.87 in/sec	ISO 294