Ultramid 8253 HS BK102 巴斯夫耐热性PA6
Ultramid® 8253 HS BK-102
Polyamide 6
BASF Corporation
产品说明：
Ultramid 8253 HS BK-102 is a heat stabilized, pigmented black, impact modified type 6 nylon graft copolymer developed for both injection molding and extrusion applications. It exhibits varying levels of toughness and flexibility combined with excellent thermal and chemical properties.
Applications
Ultramid 8253 HS BK-102 is generally recommended for applications such as plugs, receptacles, flexible connector covers, weed trimmer components, clips fasteners, flanges, key housings as well as many flexible tubing applications.
物性信息：
| 黄卡编号 | E36632-231135 |
| 添加剂 | 冲击改性剂 热稳定剂 |
| 特性 | 冲击改性 共聚物 良好的柔韧性 耐化学性良好 耐热性，高 热稳定性 韧性良好 |
| 用途 | 保护性遮盖物 草坪和园林设备 插头 管件 紧固件 外壳 |
| 机构评级 | EC 1907/2006 (REACH) |
| RoHS 合规性 | RoHS 合规 |
| 外观 | 黑色 |
| 形式 | 粒子 |
| 加工方法 | 挤出 注射成型 |
| 比重 | 1.09 | g/cm³ | ASTM D792, ISO 1183 |
| 收缩率 - 流动 (3.18 mm) | 1.2 | % | |
| 吸水率 | |||
| 24 hr | 1.5 | % | ASTM D570 |
| 23°C, 24 hr | 1.5 | % | ISO 62 |
| 饱和 | 8.1 | % | ASTM D570 |
| 饱和, 23°C | 8.1 | % | ISO 62 |
| 平衡, 50% RH | 2.3 | % | ASTM D570 |
| 平衡, 23°C, 50% RH | 2.3 | % | ISO 62 |
| 洛氏硬度 (R 级) | 82 | ASTM D785 |
| 拉伸模量 (23°C) | 2400 | MPa | ISO 527-2 |
| 抗张强度 | |||
| 屈服, 23°C | 65.0 | MPa | ASTM D638 |
| 屈服, 23°C | 60.0 | MPa | ISO 527-2 |
| 伸长率 | |||
| 屈服, 23°C | 4.0 | % | ASTM D638, ISO 527-2 |
| 断裂, 23°C | > 100 | % | ASTM D638 |
| 标称拉伸断裂应变 (23°C) | 40 | % | ISO 527-2 |
| 弯曲模量 | |||
| 23°C | 2270 | MPa | ASTM D790 |
| 23°C | 1900 | MPa | ISO 178 |
| 弯曲强度 | |||
| 23°C | 85.0 | MPa | ASTM D790 |
发布时间：2024-11-30
展开全文
其他新闻
- Ultramid 8233G HS 巴斯夫 2024-11-30
- Ultramid 8232G HS FR BK102 2024-11-30
- Ultramid 8202C HS BK102 2024-11-30
- Ultramid 8202 HS 德国巴斯夫 2024-11-30
- 美国杜邦PA66供应商实惠原厂保证 2024-11-30
- Zytel FG101 NC010 美国杜邦保证原厂原包 2024-11-30
- Zytel E51HSB NC010 杜邦公司 2024-11-30
- Zytel BM70G20HSLX BK537 2024-11-30
- Zytel 80G43HS1L BK104 2024-11-30
- Zytel 80G33L NC010 尼龙66（PA66）树脂材料 2024-11-30