Covestro Makrolon® 6267 Polycarbonate, Flame Retardant Grade
Polycarbonate, Molded
Covestro
产品说明：
ISO 7391-PC,MFLR,(,,)-18-9
Formerly Makrolon DP1-1872
MVR (300 °C/1.2 kg) 19 cm3/10 min
Flame retardant
UL 94V-0/1.5 mm
Low viscosity
UV stabilized
Easy release
Injection molding - Melt temperature 280 - 320 °C
Available in opaque colors only
Preprocessing
| Max. Water content |
物性信息：
| 密度 | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183 |
| 1.02 g/cc @Temperature 280 °C | 0.0368 lb/in³ @Temperature 536 °F | Melt | |
| 吸水率 | 0.30 % | 0.30 % | Similar to ISO 62 |
| 平衡吸湿 | 0.12 % | 0.12 % | Similar to ISO 62 |
| 线性成型收缩率,Flow | 0.0070 cm/cm | 0.0070 in/in | ISO 294-4,2577 |
| 线性成型收缩率，横向 | 0.0070 cm/cm | 0.0070 in/in | ISO 294-4,2577 |
| 熔体流动速率 | 19 g/10 min @Load 1.20 kg, Temperature 300 °C | 19 g/10 min @Load 2.65 lb, Temperature 572 °F | ISO 1133 |
| 抗张强度(屈服) | 67.0 MPa | 9720 psi | ISO 527-1/-2 |
| 伸长率 (断裂) | >= 50 % | >= 50 % | Nominal; ISO 527-1/-2 |
| 屈服伸长率 | 6.0 % | 6.0 % | ISO 527-1/-2 |
| 拉伸模量 | 2.45 GPa | 355 ksi | ISO 527-1/-2 |
| 简支梁无缺口冲击强度 | NB | NB | ISO 179/1eU |
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ISO 179/1eU | |
| 冲击 | 5000 | 5000 | Puncture - maximum force (N); ISO 6603-2 |
| 5900 @Temperature -30.0 °C | 5900 @Temperature -22.0 °F | Puncture - maximum force (N); ISO 6603-2 | |
| 多轴向仪器化冲击能量 | 50.0 J | 36.9 ft-lb | ISO 6603-2 |
| 55.0 J @Temperature -30.0 °C | 40.6 ft-lb @Temperature -22.0 °F | ISO 6603-2 |
| 体积电阻率 | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 |
| 表面电阻 | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 |
| 介电常数 | 3.0 @Frequency 1.00e+6 Hz | 3.0 @Frequency 1.00e+6 Hz | IEC 60250 |
| 3.1 @Frequency 100 Hz | 3.1 @Frequency 100 Hz | IEC 60250 | |
| 介电强度 | 34.0 kV/mm | 864 kV/in | IEC 60243-1 |
| 耗散因数 | 0.00080 @Frequency 100 Hz | 0.00080 @Frequency 100 Hz | IEC 60250 |
| 0.0090 @Frequency 1.00e+6 Hz | 0.0090 @Frequency 1.00e+6 Hz | IEC 60250 | |
| 相比耐漏电起痕指数(CTI) | 225 V | 225 V | IEC 60112 |
| 线形热膨胀系数 - 流动 | 65.0 µm/m-°C | 36.1 µin/in-°F | ISO 11359-1/-2 |
| 线性热膨胀系数,横向流动 | 65.0 µm/m-°C | 36.1 µin/in-°F | ISO 11359-1/-2 |
| 比热容 | 1.70 J/g-°C | 0.406 BTU/lb-°F | Melt |
| 导热系数 | 0.173 W/m-K | 1.20 BTU-in/hr-ft²-°F | Melt |
| 载荷下热变形温度(0.46 MPa) | 134 °C | 273 °F | ISO 75-1/-2 |
| 载荷下热变形温度(1.8 MPa) | 122 °C | 252 °F | ISO 75-1/-2 |
| 维卡软化温度 | 144 °C | 291 °F | 50°C/h 50N; ISO 306 |
| 可燃性(UL94) | V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | IEC 60695-11-10 |
| V-0 @Thickness 3.00 mm | V-0 @Thickness 0.118 in | IEC 60695-11-10 | |
| 极限氧指数 | 35 % | 35 % | ISO 4589-1/-2 |
其他新闻
- Makrolon PC 6165 PC X 科思创6265 2025-01-17
- Makrolon PC 3258 医疗级PC环氧乙烷消毒 2025-01-17
- Makrolon PC 3206 3207 3208 2025-01-17
- Makrolon PC 3152 3156 3158 2025-01-17
- Makrolon PC 3108 3107 PC MAS167 2025-01-17
- Makrolon PC 3105 3106 食品接触PC 2025-01-17
- Makrolon PC 2856 2858 2865科思创changjiazhixiao 2025-01-17
- Makrolon PC 2807 PC MAS167 2025-01-17
- Sarlink TPE RV-2668DN RV-2670D RV-2671DN NAT 2025-01-17
- Sarlink TPE RV-2240 RV-2250D BLK 111 2025-01-17
- Sarlink TPE RV-2235B RV-2235B-01 XRD 2025-01-17
- Sarlink TPE OM-2368N Teknor Apex公司 2025-01-17
- Sarlink TPE OM-2145 BLACK 404 2025-01-17
- Sarlink TPE OM-1354 橡胶取代 2025-01-17
- Sarlink TPE OM-1150N 可粘结性 2025-01-17