Ultramid 8253 HS BK102 巴斯夫耐热性PA6

发布时间： 2024-04-23 15:00 更新时间： 2025-01-29 07:02

Ultramid® 8253 HS BK-102

Polyamide 6

BASF Corporation

产品说明：

Ultramid 8253 HS BK-102 is a heat stabilized, pigmented black, impact modified type 6 nylon graft copolymer developed for both injection molding and extrusion applications. It exhibits varying levels of toughness and flexibility combined with excellent thermal and chemical properties.

Applications
Ultramid 8253 HS BK-102 is generally recommended for applications such as plugs, receptacles, flexible connector covers, weed trimmer components, clips fasteners, flanges, key housings as well as many flexible tubing applications.

物性信息：

基本信息

黄卡编号	E36632-231135
添加剂	冲击改性剂热稳定剂
特性	冲击改性共聚物良好的柔韧性耐化学性良好耐热性，高热稳定性韧性良好
用途	保护性遮盖物草坪和园林设备插头管件紧固件外壳
机构评级	EC 1907/2006 (REACH)
RoHS 合规性	RoHS 合规
外观	黑色
形式	粒子
加工方法	挤出注射成型

物理性能额定值单位制测试方法

比重	1.09	g/cm³	ASTM D792, ISO 1183
收缩率 - 流动 (3.18 mm)	1.2	%
吸水率
24 hr	1.5	%	ASTM D570
23°C, 24 hr	1.5	%	ISO 62
饱和	8.1	%	ASTM D570
饱和, 23°C	8.1	%	ISO 62
平衡, 50% RH	2.3	%	ASTM D570
平衡, 23°C, 50% RH	2.3	%	ISO 62

硬度额定值单位制测试方法

洛氏硬度 (R 级)

ASTM D785

机械性能额定值单位制测试方法

拉伸模量 (23°C)	2400	MPa	ISO 527-2
抗张强度
屈服, 23°C	65.0	MPa	ASTM D638
屈服, 23°C	60.0	MPa	ISO 527-2
伸长率
屈服, 23°C	4.0	%	ASTM D638, ISO 527-2
断裂, 23°C	> 100	%	ASTM D638
标称拉伸断裂应变 (23°C)	40	%	ISO 527-2
弯曲模量
23°C	2270	MPa	ASTM D790
23°C	1900	MPa	ISO 178
弯曲强度
23°C	85.0	MPa	ASTM D790