Fortron® 6450A6
Polyphenylene Sulfide
Celanese Corporation
玻璃矿物
产品说明：
Fortron 6450A6 is a fiberglass reinforced, mineral filled alloy that exhibits improved wear and sliding properties versus standard Fortron compounds.
物性信息：
| 填料/增强材料 |
|
| 特性 |
|
| RoHS 合规性 |
|
| 密度 | 1.58 | g/cm³ | ISO 1183 |
| 吸水率 (饱和, 23°C) | 0.020 | % | ISO 62 |
| 拉伸应力 (断裂) | 90.0 | MPa | ISO 527-2/1A/5 |
| 拉伸应变 (断裂) | 1.5 | % | ISO 527-2/1A/5 |
| 弯曲模量 (23°C) | 11000 | MPa | ISO 178 |
| 弯曲应力 (23°C) | 130 | MPa | ISO 178 |
| 摩擦系数 | ASTM D1894 | ||
| Dynamic 1 | 0.31 | ASTM D1894 | |
| Dynamic 2 | 0.34 | ASTM D1894 | |
| Static 3 | 0.37 | ASTM D1894 | |
| Static 4 | 0.31 | ASTM D1894 | |
| 与钢 - 动态 5 | 0.13 | ASTM D1894 | |
| 与钢 - 静态 6 | 0.16 | ASTM D1894 | |
| 磨损因数 7 | ASTM D3702 | ||
| 416 Stainless : 32°C | 164 | 10^-10 in³·min/ft·lb·hr | ASTM D3702 |
| C-1018 Steel : 49°C | 217 | 10^-10 in³·min/ft·lb·hr | ASTM D3702 |
| C-1018 Steel : 93°C | 300 | 10^-10 in³·min/ft·lb·hr | ASTM D3702 |
| 简支梁缺口冲击强度 (23°C) | 6.0 | kJ/m² | ISO 179/1eA |
| 简支梁无缺口冲击强度 (23°C) | 18 | kJ/m² | ISO 179/1eU |
| 悬壁梁缺口冲击强度 (23°C) | 6.0 | kJ/m² | ISO 180/1A |
| 热变形温度 | |||
| 1.8 MPa, 未退火 | 260 | °C | ISO 75-2/A |
其他新闻
- Fortron 6341L4 6345L4 高性能的PPS材料 2025-01-05
- Fortron 6165A6FC 玻璃\矿物, 65% 填料 2025-01-05
- Fortron 6165A4 FC美国塞拉尼斯 2025-01-05
- Fortron 6162A7 玻璃\矿物 2025-01-05
- Fortron 6160B4玻璃\矿物 2025-01-05
- DURAFIDE 1140A64 1140A66 1140A7 40%玻纤 2025-01-05
- DURAFIDE 1140A1 1140A6泵壳、泵轮、阀、风扇、流量计 2025-01-05
- DURAFIDE 1130T6 PPS耐冲击 2025-01-05
- 聚苯硫醚(PPS)DURAFIDE 1130A1 1130A64 30%玻璃纤维 2025-01-05
- DURAFIDE 0220A9 0220U9高韧性PPS 2025-01-05
- DIC.PPS ZL-130 30% PTFE 纤维 2025-01-05
- DIC.PPS Z-650-T6玻璃\矿物 2025-01-05
- DIC.PPS Z-230 Z-240 棕色颗粒 2025-01-05
- DIC.PPS Z-200-E5电子电器部件 2025-01-05
- 日本油墨DIC.PPS FZL-4033正牌料 2025-01-05