Celcon M90UV POM抗紫外线性能良好
发布时间： 2024-04-12 10:41 更新时间： 2024-11-28 07:02
Celcon® M90UV
Acetal (POM) Copolymer
Celanese Corporation
产品说明：
Celcon® M90UV is an acetal copolymer developed as a natural UV light stabilized standard flow grade for overall performance in most molding applications. It has been formulated as a natural acetal that does not discolor, yet maintains protection from UV light exposure.
物性信息：
| 黄卡编号 |
|
| 添加剂 |
|
| 特性 |
|
| 用途 |
|
| RoHS 合规性 |
|
| 外观 |
|
| 加工方法 |
|
| 比重 | 1.41 | g/cm³ | ASTM D792, ISO 1183 |
| 溶化体积流率（MVR） (190°C/2.16 kg) | 8.00 | cm³/10min | ISO 1133 |
| 收缩率 | ASTM D955 | ||
| 流动 | 2.2 | % | ASTM D955 |
| 横向流动 | 1.8 | % | ASTM D955 |
| 吸水率 | ISO 62 | ||
| 饱和, 23°C | 0.75 | % | ISO 62 |
| 平衡, 23°C, 50% RH | 0.20 | % | ISO 62 |
| 拉伸模量 | 2600 | MPa | ISO 527-2/1A/1 |
| 抗张强度 | |||
| 屈服, 23°C | 60.7 | MPa | ASTM D638 |
| 屈服 | 65.0 | MPa | ISO 527-2/1A/50 |
| 拉伸应变 (屈服) | 10 | % | ISO 527-2/1A/50 |
| 弯曲模量 (23°C) | 2550 | MPa | ISO 178 |
| 简支梁缺口冲击强度 (23°C) | 6.1 | kJ/m² | ISO 179/1eA |
| 悬壁梁缺口冲击强度 (23°C) | 5.8 | kJ/m² | ISO 180/1A |
| 载荷下热变形温度 | |||
| 1.8 MPa, 未退火 | 110 | °C | ASTM D648 |
| 1.8 MPa, 未退火 | 101 | °C | ISO 75-2/A |
| 熔融温度 1 | 165 | °C | ISO 11357-3, ASTM D3418 |
| 线形热膨胀系数 | ISO 11359-2 | ||
| 流动 | 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| 横向 | 1.2E-4 | cm/cm/°C | ISO 11359-2 |
其他新闻
- Celcon M90 POM薄壁 2024-11-28
- Celcon M90SW POM材料供应商 2024-11-28
- Celcon M90AW 齿轮用pom耐磨 2024-11-28
- Celcon M90-45XAP 聚甲醛POM 2024-11-28
- Celcon M90-45H F1抗紫外线POM 2024-11-28
- Celcon M90-34 POM物性表 2024-11-28
- Celcon M90-07 POM泰科纳 2024-11-28
- 美国塞拉尼斯POM代理商Celanese 2024-11-28
- Celcon M50 Acetal (POM) 2024-11-28
- Celcon M450 齿轮和轴承POM 2024-11-28
- Celcon M270 M270UV 紫外线稳定 2024-11-28
- Celcon M25 M25UV 耐疲劳POM 2024-11-28
- Celcon M15HP 美国塞拉尼斯OM 2024-11-28
- Celcon M140 M140-L1 Celanese代理商 2024-11-28
- Celcon LW90 LW90-F2 LW90FS-K LW90-S2 LW90-SC 2024-11-28