公司新闻
Hostaform S 9243 XAP2 LS
发布时间： 2024-04-16 10:31 更新时间： 2024-06-07 07:02
Hostaform® S 9243 XAP² ™ LS
Acetal (POM) Copolymer
Celanese Corporation
产品说明：
POM copolymer, modified
Injection molding type, elastomer-containing; with higher impact
strength and slightly lower hardness, rigidity and chemical
resistance than the basic type HOSTAFORM C 9021
Reduced emission grade, Emission according to VDA 275 < 5 mg/kg
good weld strength.
Burning rate according to FMVSS 302 < 100 mm/min (1 mm thickness)
Preliminary Datasheet for natural and colored grades
物性信息：
| 黄卡编号 |
|
| 添加剂 |
|
| 特性 |
|
| RoHS 合规性 |
|
| 外观 |
|
| 密度 | 1.33 | g/cm³ | ISO 1183 |
| 溶化体积流率（MVR） (190°C/2.16 kg) | 4.00 | cm³/10min | ISO 1133 |
| 收缩率 | ISO 294-4 | ||
| 垂直流动方向 | 1.8 | % | ISO 294-4 |
| 流动方向 | 1.9 | % | ISO 294-4 |
| 吸水率 (饱和, 23°C) | 1.0 | % | ISO 62 |
| 拉伸模量 | 1950 | MPa | ISO 527-2/1A/1 |
| 拉伸应力 (屈服) | 44.0 | MPa | ISO 527-2/1A/50 |
| 拉伸应变 (屈服) | 9.0 | % | ISO 527-2/1A/50 |
| 标称拉伸断裂应变 | 40 | % | ISO 527-2/1A/50 |
| 拉伸蠕变模量 | ISO 899-1 | ||
| 1 hr | 1700 | MPa | ISO 899-1 |
| 1000 hr | 950 | MPa | ISO 899-1 |
| 弯曲模量 (23°C) | 1850 | MPa | ISO 178 |
其他新闻
- Hostaform S 27242 XAP2 2024-11-28
- Hostaform S 27072 WS 10/1570 2024-11-28
- Hostaform S 27064 XAP2 物性表POM 2024-11-28
- Hostaform S 27063 Celanese 2024-11-28
- Hostaform EC270TX 传导性POM导电 2024-11-28
- Hostaform EC141SXF 10/9022 POM导电级 2024-11-28
- Hostaform EC140XF 导电POM防静电 2024-11-28
- Hostaform EC140CF10 碳纤维导电POM 2024-11-28
- Hostaform CP15X 高刚性POM 2024-11-28
- Hostaform C 9021 XAP2 LS 低气味POM 2024-11-28
- Hostaform C 9021 TF XAP2 PTFE润滑剂POM 2024-11-28
- Hostaform C 9021 SW XAP2 LS 减声器POM 2024-11-28
- Hostaform C 9021 S OEK 硅酮润滑剂POM 2024-11-28
- Hostaform C 9021 MD POM特性 2024-11-28
- Celcon MC270-HM POM比重收缩率吸水率 2024-11-28