Hostaform TF-10XAP
发布：2024-04-17 10:33，更新：2024-05-21 07:02
Hostaform® TF-10XAP®
Acetal (POM) Copolymer
Celanese Corporation
产品说明：
Hostaform® acetal copolymer TF-10 XAP® is low emission, improved flow, impact modified grade providing optimum performance in general purpose injection molding primarily for the interior automotive market. This grade provides overall excellent performance with improved impact in many applications.
物性信息：
| 添加剂 |
|
| 特性 |
|
| 用途 |
|
| RoHS 合规性 |
|
| 加工方法 |
|
| 密度 | 1.38 | g/cm³ | ISO 1183 |
| 溶化体积流率（MVR） (190°C/2.16 kg) | 13.0 | cm³/10min | ISO 1133 |
| 收缩率 | ISO 294-4 | ||
| 垂直流动方向 | 1.9 | % | ISO 294-4 |
| 流动方向 | 2.1 | % | ISO 294-4 |
| 拉伸模量 | 1750 | MPa | ISO 527-2/1A/1 |
| 拉伸应力 (屈服) | 49.0 | MPa | ISO 527-2/1A/50 |
| 拉伸应变 (屈服) | 13 | % | ISO 527-2/1A/50 |
| 弯曲模量 (23°C) | 1700 | MPa | ISO 178 |
| 简支梁缺口冲击强度 | ISO 179/1eA | ||
| -30°C | 7.0 | kJ/m² | ISO 179/1eA |
| 23°C | 10 | kJ/m² | ISO 179/1eA |
| 热变形温度 | |||
| 0.45 MPa, 未退火 | 139 | °C | ISO 75-2/B |
| 1.8 MPa, 未退火 | 75.0 | °C | ISO 75-2/A |
| 熔融温度 1 | 165 | °C | ISO 11357-3 |
| 干燥温度 | 80.0 到 100 | °C | |
| 干燥时间 | 3.0 | hr | |
| 料筒后部温度 | 170 到 180 | °C |
其他新闻
- Hostaform SXT90Z-01 XAP 2024-05-21
- Hostaform SlideX C0313 XAP2 2024-05-21
- Hostaform SlideX C0304 XAP2 2024-05-21
- Hostaform S 9364LPB 2024-05-21
- Hostaform S 9364 XAP2美国塞拉尼斯POM代理商Celanese 2024-05-21
- Hostaform S 9364 WS 10/1570 2024-05-21
- Hostaform S 9363 XAP2 2024-05-21
- Hostaform S 9362 XAP2 2024-05-21
- Hostaform S 9244 XAP2 LS 2024-05-21
- Hostaform S 9243 XAP2 LS 2024-05-21
- Hostaform S 27242 XAP2 2024-05-21
- Hostaform S 27072 WS 10/1570 2024-05-21
- Hostaform S 27064 XAP2 物性表POM 2024-05-21
- Hostaform S 27063 Celanese 2024-05-21
- Hostaform EC270TX 传导性POM导电 2024-05-21