Makrolon® FU1007
Polycarbonate
Covestro - Polycarbonates
产品说明:
MVR (300 °C/1.2 kg) 9.0 cm³/10 min; special grade for furniture applications with demands regarding fire standards UNI 8456, 8457, 9174 and 9175; medium viscosity; UV stabilized; easy release; injection molding - melt temperature 280 - 320 °C; available in transparent, translucent and opaque colors
物性信息:
添加剂 |
|
特性 |
|
用途 |
|
机构评级 |
|
RoHS 合规性 |
|
外观 |
|
加工方法 |
|
密度 (23°C) | 1.20 | g/cm³ | ISO 1183 |
熔流率(熔体流动速率) (300°C/1.2 kg) | 10 | g/10 min | ISO 1133 |
溶化体积流率(MVR) (300°C/1.2 kg) | 9.00 | cm³/10min | ISO 1133 |
收缩率 | |||
垂直流动方向 | 0.60 到 0.80 | % | ISO 2577 |
流动方向 | 0.60 到 0.80 | % | ISO 2577 |
垂直流动方向 : 2.00 mm 1 | 0.70 | % | ISO 294-4 |
流动方向 : 2.00 mm 2 | 0.65 | % | ISO 294-4 |
吸水率 | ISO 62 | ||
饱和, 23°C | 0.30 | % | ISO 62 |
平衡, 23°C, 50% RH | 0.12 | % | ISO 62 |
球压硬度 | 116 | MPa | ISO 2039-1 |
拉伸模量 (23°C) | 2400 | MPa | ISO 527-2/1 |
拉伸应力 | ISO 527-2/50 | ||
屈服, 23°C | 67.0 | MPa | ISO 527-2/50 |
断裂, 23°C | 70.0 | MPa | ISO 527-2/50 |
拉伸应变 | ISO 527-2/50 | ||
屈服, 23°C | 6.1 | % | ISO 527-2/50 |
断裂, 23°C | 120 | % | ISO 527-2/50 |
标称拉伸断裂应变 (23°C) | > 50 | % | ISO 527-2/50 |
拉伸蠕变模量 | ISO 899-1 | ||
1 hr | 2200 | MPa | ISO 899-1 |
1000 hr | 1900 | MPa | ISO 899-1 |
弯曲模量 3(23°C) | 2400 | MPa | ISO 178 |
弯曲应力 4 | ISO 178 | ||
3.5% 应变, 23°C | 74.0 | MPa | ISO 178 |
23°C | 98.0 | MPa | ISO 178 |
Flexural Strain at Flexural Strength (23°C) 5 | 7.0 | % | ISO 178 |
其他新闻
- Makrolon PC GF8001 2024-05-07
- Makrolon PC FR7087 2024-05-07
- Makrolon PC FR6002 2024-05-07
- Makrolon PC FP3087 2024-05-07
- Makrolon PC ET3227 2024-05-07
- Makrolon PC ET3137 2024-05-07
- Makrolon PC ET3117 Covestro 2024-05-07
- Makrolon PC ET3113 2024-05-07
- Makrolon PC ET2613 2024-05-07
- Makrolon PC ET PC UV540 2024-05-07
- Makrolon PC ET PC UV530 2024-05-07
- Makrolon PC ET PC UV510 2024-05-07
- Makrolon PC ET PC UV130 2024-05-07
- Makrolon PC ET PC UV120 2024-05-07
- Makrolon PC ET PC UV112 2024-05-07